Which discontinuity is likely to be found in sand castings?

The correct answer highlights shrinkage as a common discontinuity found in sand castings. During the solidification process of molten metal, it undergoes thermal contraction as it cools. If the casting does not have proper feeding mechanisms or is not designed to accommodate this shrinkage, voids or cavities can form within the casting. This type of discontinuity can compromise the integrity and strength of the final product.

In sand casting, because the material is poured into a mold made of sand, control over how the metal cools can be challenging. Therefore, shrinkage cavities are often encountered unless specific measures are taken during the casting process, such as designing the mold to include risers that compensate for this shrinkage as the metal solidifies.

The other discontinuities mentioned might occur in different casting methods or are less typical in sand casting, but shrinkage is especially notable in this context due to the nature of the process and the materials involved.